Comparative Study of Four-Point Measurements of Copper Thin Films Resistivity in Aligned and Square Configuration at Low Frequencies
Journal of Engineering Research and Reports,
The main objective of this research work is the comparison of the two Van Der Pauw four-point measurement configurations (aligned and square) commonly used to measure the resistivity of metal thin films which are widely used in the manufacture of planar components such as inductors, transformers, insulators, circulators, etc. Electrical characterization is very important because it ensures the quality of the metal supposed to conduct electrical current in the components mentioned above.
The resistivity measured by using the square or aligned configuration sometimes has significant differences. Making a comparative study therefore allow to know which gap between points, which frequencies to choose when measurements must be made by using square or aligned configuration.
In this paper, the measured thin films are made of copper which is broadly used in the structures because of its physical, chemical and mechanical properties . The copper is deposited on alumina substrates by magnetron radiofrequency sputtering. Rectangular alumina substrates of dimensions 50mm x 20mm x 635μm were used. Thin film resistivity measurements using a four-point measurement method were performed by using HP 4284A LCRmeter in the frequency range of a few Hz to a few kHz. The comparison was made between the four-point aligned method and the four-point square method based on the frequency, the gap between points and the thin film thickness was made.
The results obtained by the study show that both configurations measure the same resistivity up to 1 kHz and then the increase of resistivity in aligned configuration limits its use beyond this frequency. The square configuration can still measure the same resistivity up to 40 kHz. The study also shows that the gap between points is limited to 3 μm in aligned configuration while the square configuration allows a gap up to 5 μm.
- Thin films
- Van Der Pauw
How to Cite
Allassem Désiré. Contribution to the realization of a planar micro-inductor. PhD Thesis in Optics, Photonics, Microwave, Saint-Etienne: Jean Monnet University. 2010;117.
Yacoub Nassian Nimir. Measurement of metal thin films resistivity, comparison between the four-point method and the square points method. Research master's thesis in electronics, n’djamena: consortium of universities of chad and jean monnet university of saint-etienne, National Higher Institute of Science and Technology of Abéché. 2018;52.
Yaya Dagal Dari. Design, realization and characterization of planar inductors with magnetic film. PhD Thesis in Optics, Photonics, Microwave, Saint-Etienne: Jean Monnet University, 2013;167.
Matibeye Alain, Electrical characterization of thin films through its conductivity. Research master's thesis in electronics, n’djamena: consortium of universities of chad and jean monnet university of saint-etienne, university institute of science and technology of Abéché. 2013;50.
Abbas Mahamat Sied Haggar. Electrical characterization of copper thin films in low frequency using the LCRmeter. Research master's thesis in electronics, n’djamena: consortium of universities of chad and jean monnet university of saint-etienne, national higher institute of science and technology of Abéché. 2015;55.
Djerandouba Bayombaye. Measurement of metal thin films resistivity, study of the corrective factor of the Van der Pauw method. Research master's thesis in electronics, n’djamena: Consortium of universities of chad and jean monnet university of saint-etienne, national higher institute of science and technology of Abéché. 2017;56.
Jean-Pierre Chatelon. Magnetic thin films developed by RF sputtering. Micro-technology lecture notes, Saint-Etienne: Jean Monnet Université; 2008.
A. Mennad. Les techniques de dépôt des couches minces et leurs applications. Revue des Energies renouvelables. 2015; 18(4)713-719.
Noua Bouhssira. Development and characterization of zinc oxide thin films by evaporation. PhD Thesis in Physics, Constantine: University of Mentouri. 2005; 104.
Stéphane Andrieu. Introduction to thin films and Networks. Franco-Romanian School: Magnetism of nanoscopic systems and hybrid structures, Materials Physics Laboratory, Brasov. 2003;6.
F.M. Smits. Measurement of sheet resistivites with the four-point probe. The Bell System Technical Journal. 1957;171-178.
F.M. Smits. Measurement of sheet resistivites with the four-point probe. The Bell System Technical Journal. 1958;711-718.
Valdes LB, Member,IRE. Resistivity measurements on germanium for transistors. Proceedings of IRD. 1954;420-427.
Mike Bolt, Calvin College. Van der Pauw’s Theorem on Sheet Resistance. Annual Meeting of the Michigan MAA Hope College. 2015;24.
Maria P, Gutierrez, Haiyong Li, Jeffrey Patton. Thin film surface resistivity. Mate 210 Experimental Methods in Materials Engineering. 2002;25.
Abstract View: 260 times
PDF Download: 52 times